Polyol and Isocynate for the PU foam shoe insole pad
JYXC－01A/B
Introduction:
JYXC-01A is made up of polymer polyol, grafted polyether polyol, cross linker, blowing agent, and composite catalyst which contains some biology base component. JYXC-01B is made up of MDI.
This PU system has good liquidity which is suitable for the production of PU shoe insole pad. The finished product has a excellent physical property and with some biodegradability which is eco-friendly.
Typical Properties
| Item Unit | JYXC-01A | JYXC-01B | |
| Appearance NCO Viscosity(25℃)Density (20℃) Storage temp. Shelf life |
% mpa.s g/ml ℃ Months | Milky white liquid / 1800±200 1.05±0.05 15－25 6 | Transparent liquid 23±1 600±15 1.2±0.05 15－25 6 |
Recommended ratio
| Weight ratio | |
| 100 90-120 |
REACTIVE PROPERTY (Material temperature is 25℃)
| By hand | Machine | ||
| Cream time (s) Gel time (s) Mold temperature (℃) Demould time (min)FRD (kg/m3) | s s ℃ min kg/m3 | 30±5 95±5 30-40 25-30 80-90 | 28±5 90±5 30-40 25-30 75-85 |
TYPICAL PHYSICAL PROPERTY
| Unit | Data | |
| Moulded density Tensile strength Elongation (%) Rebound Tear strength Hardness
| Kg/m3 Kpa % % KN/m Shore C
| 85-130 ≥450 ≥70 25-35 ≥0.25 25-35
|
The final interpretation of this specification is owned by our company.